CUMIFRAC M

CUMIFRAC M are produced from silicon carbide, a raw material synthesized in a resistance-type electric furnace at temperature exceeding 2500°C, through the reaction of silica with carbon. They have a thermal conductivity 10 times that of fireclay refractories, good corrosion and thermal shock resistance, and can be formed into complex shapes. They can withstand attack and flame erosion. This makes CUMIFRAC unusual even among advanced refractories and has given it wide uses.

 

industries

  • H.T. Insulators / Ceramics
  • Sanitaryware
  • Ferro Alloys
  • Foundries, Forge Plants, Powder metallurgy

features

  • Extremely high thermal conductivity
  • Very high hot strength
  • High erosion and abrasion resistance
  • Thermal shock resistance
  • Chemical inertness

application

  • Kiln furniture
  • Muffles and chamber fronts
  • Taphole linings
  • Heat treatment furnace hearth

Properties

PropertiesUNITLimit ValueTypical Value
Maximum Hot Face Temperature°C15001500
Bulk Densitygm/cc2.50 min.2.55
Apparent Porosity%18.0 max.16.0
Cold Crushing StrengthKg/cm2700 min.850
Modulus of Rupture   
At Room TemperatureKg/cm2175 min.180
At 1250°CKg/cm2100 min.125
Thermal Conductivity At 1000°C Hot Face TemperatureW/m°K15.0 min15.7
Chemical Analysis   
SiC%82.0 min.85.38
Al2O3%1.0 max0.60
Fe2O3%1.0 max.0.64